300g Biaxial Fiberglass Fabric
Product Details
Product name |
300g Biaxial Fiberglass Fabrics |
Short Description: |
Biaxial Glass Fiber Fabric is a high-performance textile that combines exceptional strength with remarkable flexibility. It can be with mat or without mat It is ideal for applications such as wind industry, aerospace, automotive, marine, construction |
MOQ |
≥100Sqm |
Acceptance |
OEM/ODM, Trade, Wholesale |
Payment Method |
T/T, PayPal, L/C |
Feature |
1.No any Binder, good compatible with Multi-Resin 3.Easy workability and low cost |
Product Information
Product No. |
Area Density |
+45°Roving Density |
-45°Roving Density |
Width |
Roll Length |
（g/m2） |
（g/m2） |
（g/m2） |
（mm） |
（m） |
|
BX220-127 |
220±20 |
1.5g(68tex) |
110g(100tex) |
1270±5 |
178 |
BX300-127 |
300±20 |
1.5g(68tex) |
150g(25k) |
1270±5 |
131 |
BX450-127 |
450±20 |
1.5g(68tex) |
225g(600tex) |
1270±5 |
87 |
Product Specification
|
Product Code |
BX300-1270 | Density (g/m2) | 308(±5%) |
|---|---|---|---|
| Fiber Architecture |
2（±45°） |
Width(mm) | 1270mm |
| Stitching Type | 6.0 | Moisture Content(%) | ≤0.2 |
| Compatible Resin | SILANE | Loss on Ignition (%) | 0.4-0.8 |
|
Breaking Strength in Warp(N/25mm) |
＞300 | Breaking Strength in Warp(N/25mm) | ＞80 |
Application
Applications of 300g Biaxial Fiberglass Fabrics
1. Construction and Infrastructure: Used for reinforcement in concrete and masonry to increase strength and durability against weathering and seismic activity.
2. Automotive Industry: Biaxial fabrics are utilized in the production of automotive parts for their light weight and high strength properties, enhancing vehicle performance and safety.
3. Aerospace: In aerospace applications, these fabrics contribute to the structural integrity of aircraft components, often in areas where weight reduction and strength are critical.
4. Marine Applications: Fiberglass fabrics are ideal for boat building and repair, offering resistance to water, salt, and UV damage.
5. Electrical Insulation: Due to their non-conductive nature, they are used in the creation of electrical insulation components to prevent electrical faults.
6. Wind Energy: Biaxial fabrics are employed in the construction of wind turbine blades for their ability to withstand the forces exerted during operation.
Storing Biaxial Fiberglass Fabrics: A Guide
1. Clean and Dry Environment: Biaxial fiberglass fabrics should be stored in a clean and dry environment to prevent any moisture-related damage or contamination from dust and dirt.
2. Temperature Control: It's important to maintain a stable temperature. Extreme heat or cold can affect the fabric's integrity. A temperature range of 60-80°F (15-27°C) is typically recommended.
3. Humidity Levels: Keep humidity levels low to avoid moisture absorption. A relative humidity below 60% is ideal.
4. Proper Stacking: Stack the rolls of fabric in a way that prevents them from crushing or bending. Use pallets or sturdy shelves to support the weight and maintain the rolls' shape.
5. Avoid Direct Sunlight: Prolonged exposure to sunlight can cause the fabric to degrade. Store the rolls in a shaded area or within a closed storage unit.
6. Protection from Pests: Use pest control measures to prevent damage from insects or rodents, which can chew through the fabric.
Remarks
Standard width: 120cm,125cm, Max.width 260cm. Min.width 10cm
tandard Roll weight: 50 or 55kg
Packaging
Each roll is wound on paper tube (3”Dia.) with plastic film and packed in individual cardboard box.
16 or 12 cartons per Pallet.
description1